Liquid (meth)acrylic composition comprising a multistage polymer and a (meth)acrylic monomer, its method of preparation and its use

ABSTRACT

The present invention relates to a liquid (meth) acrylic composition comprising a (meth) acrylic monomer, a (meth) acrylic polymer and a multistage polymer. In particular the present invention it relates to liquid composition comprising a (meth) acrylic monomer, a (meth) acrylic polymer and a multistage polymer that can be used as a syrup and especially as a syrup for impregnation. More particularly the present invention relates also to a process for preparing a liquid composition comprising a (meth) acrylic monomer, a (meth) acrylic polymer and a multistage polymer.

FIELD OF THE INVENTION

The present invention relates to a liquid (meth)acrylic compositioncomprising a (meth)acrylic monomer, a (meth)acrylic polymer and amultistage polymer.

In particular the present invention it relates to liquid compositioncomprising a (meth)acrylic monomer, a (meth)acrylic polymer and amultistage polymer that can be used as a syrup and especially as a syrupfor impregnation.

More particularly the present invention relates also to a process forpreparing a liquid composition comprising a (meth)acrylic monomer, a(meth)acrylic polymer and a multistage polymer.

Technical Problem

Impact modifiers are widely used to improve the impact strength forpolymeric compositions with the aim to compensate their inherentbrittleness or the embrittlement that occurs at ambient temperature butalso and especially sub zero temperatures, notch sensitivity and crackpropagation. So an impact modified polymer is a polymeric material whoseimpact resistance and toughness have been increased by the incorporationof phase micro domains of a rubbery material.

This is usually done due to the introduction of microscopic rubberparticles into the polymer matrix that can absorb the energy of animpact or dissipate it. One possibility is to introduce the rubberparticles in form of core-shell particles. These core-shell particlesthat possess very generally a rubber core and a polymeric shell, havingthe advantage of a proper particle size of the rubber core for effectivetoughening and the grafted shell in order to have the adhesion andcompatibility with the thermoplastic matrix.

The performance of the impact modification is a function of theparticles size, especially of the rubber part of the particle, and itsquantity. There is an optimal average particle size in order to have thehighest impact strength for a given quantity of added impact modifierparticles.

These primary impact modifier particles are usually added in form ofpowder particles to the polymeric material. These powder particles areagglomerated primary impact modifier particles. During the blending ofthe thermoplastic material with the powder particles the primary impactmodifier particles are regained and are dispersed more or lesshomogenously dispersed in the thermoplastic material.

While the particle size of the impact modifier particles in the range ofnanometers, the range of the agglomerated powder particles is in therange of micrometers. Latter is much easier for handling.

For many polymers, thermoplastic or thermoset polymers it is verydifficult or nearly impossible to disperse correctly these multistagepolymer in form of core shell particles as agglomerated dry powders. Anideal homogenous dispersion of the core-shell particle has noagglomerates after the dispersion in the thermoplastic material alsocalled matrix.

This is even more difficult if the multistage polymers should behomogenously distributed in a polymeric matrix which comprises also afibrous substrate as for example fibre reinforced polymeric composites.

The fibrous substrate is usually impregnated by a liquid composition,either a molten polymer or a liquid composition comprising monomers,oligomers and/or polymers.

The objective of the present invention is to obtain liquid compositioncomprising a (meth)acrylic monomer, a (meth)acrylic polymer and amultistage polymer, with a homogenous dispersion of the multistagepolymer.

An objective of the present invention is also to have a liquidcomposition comprising a (meth)acrylic monomer, a (meth)acrylic polymerand a multistage polymer, with a homogenous dispersion of the multistagepolymer, that can be used in a polymerization process.

Another objective of the present invention is to avoid or reducesignificantly the agglomeration of multistage polymer.

Still an additional objective is having a process for preparing a liquidcomposition comprising a (meth)acrylic monomer, a (meth)acrylic polymerand a multistage polymer, with a homogenous dispersion of the multistagepolymer.

Still a further objective is the use of the composition comprising amonomer, a (meth)acrylic polymer for the impact modification ofpolymers.

Still a further objective is to obtain liquid composition comprising a(meth)acrylic monomer, a (meth)acrylic polymer and a multistage polymer,with a homogenous dispersion of the multistage polymer as impregnationliquid for a fibrous substrate or the use the liquid composition in animpregnation process for impregnating a fibrous substrate.

Still another objective of the present invention is to wet completely,correctly and in a homogenous way a fibrous substrate duringimpregnation with a liquid composition comprising a multistage polymer.

BACKGROUND OF THE INVENTION Prior Art

The document WO2014/013028 discloses an impregnation process for afibrous substrate, a liquid (meth) acrylic syrup for the impregnationprocess, its method of polymerization and structured article obtainedthereof. The syrup comprises a (meth)acrylic monomer, a (meth)acrylicpolymer and optionally impact modifier in the form of fine particles.

The document WO2014/135815 discloses a viscous liquid (meth)acrylicsyrup mainly containing methacrylic or acrylic components and animpact-modifying additive for reinforcing the impact strength of athermoplastic material obtained after polymerization of the syrup. Theimpact-modifying additive is based on elastomeric domains consisting ofmacromolecular blocks of flexible nature. A multi stage polymerespecially in form of core/shell particles is not disclosed.

The document WO2014/135816 discloses a viscous liquid (meth)acrylicsyrup mainly containing methacrylic or acrylic components and organic ormineral fillers intended to reduce the proportion of residual monomerafter polymerization of the (meth)acrylic syrup. The organic filler ischosen from crosslinked PMMA beads. A multi stage polymer especially inform of core/shell particles is not disclosed.

None of the prior art documents discloses a composition as claimed or aprocess for obtaining it or its use.

BRIEF DESCRIPTION OF THE INVENTION

Surprisingly it has been found that a liquid composition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) a (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer (M1) ratio by weight        in the liquid composition is between 1/99 and 25/75, is less        viscous than a composition not comprising the(meth)acrylic        polymer (P1).

Surprisingly it has also been found that a liquid composition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) a (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer (M1) ratio by weight        in the liquid composition is between 1/99 and 25/75, possesses a        better dispersion of the multistage polymer than a composition        not comprising the(meth)acrylic polymer (P1).

Surprisingly it has also been found that a liquid composition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) a (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer (M1) ratio by weight        in the liquid composition is between 1/99 and 25/75, can be used        to prepare a better dispersion of the multistage polymer in the        monomer (M1) than a composition not comprising the(meth)acrylic        polymer (P1).

Surprisingly it has also been found that a process for manufacturing aliquid composition comprising the steps of

-   -   a) preparing a composition comprising a the (meth) acrylic        polymer (P1) and a multi stage polymer    -   b) mixing the composition of previous step with a (meth)acrylic        monomer (M1)        wherein the multistage polymer to monomer (M1) ratio by weight        in the liquid composition is between 1/99 and 25/75, yields to a        liquid composition that is less viscous than a composition not        comprising the(meth)acrylic polymer (P1).

Surprisingly it has also been found that a process for manufacturing aliquid composition comprising the steps of

-   -   a) preparing a composition comprising a the (meth) acrylic        polymer (P1) and a multi stage polymer    -   b) mixing the composition of previous step with a (meth)acrylic        monomer (M1)        wherein the multistage polymer to monomer (M1) ratio by weight        in the liquid composition is between 1/99 and 25/75, yields to a        impregnation liquid in form of a (meth) acrylic syrup.

Surprisingly it has also been found that a liquid composition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) a (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer ratio by weight in the        liquid composition is between 1/99 and 25/75, can be used for        impregnating a fibrous substrate.

Surprisingly it has also been found that a liquid composition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) a (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer ratio by weight in the        liquid composition is between 1/99 and 25/75, can be used in        impregnation process for impregnating a fibrous substrate,        wherein said fibrous substrate is made of long fibres.

DETAILED DESCRIPTION OF THE INVENTION

According to a first aspect, the present invention relates to a liquidcomposition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) a (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer ratio by weight in the        liquid composition is between 1/99 and 25/75.

According to a second aspect, the present invention relates to a processfor manufacturing a liquid composition comprising the steps of

-   -   a) preparing a composition comprising a the (meth) acrylic        polymer (P1) and a multi stage polymer    -   b) mixing the composition of previous step with a (meth)acrylic        monomer (M1)        wherein the multistage polymer to monomer ratio by weight in the        liquid composition is between 1/99 and 25/75.

In a third aspect the present invention relates to the use a liquidcomposition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) a (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer ratio by weight in the        liquid composition is between 1/99 and 25/75, for impregnating a        fibrous substrate.

In a forth aspect the present invention relates to the use a liquidcomposition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) a (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer ratio by weight in the        liquid composition is between 1/99 and 25/75, in an impregnation        process for impregnating a fibrous substrate, wherein said        fibrous substrate is made of long fibres.

By the term “polymer powder” as used is denoted a polymer comprisingpowder grain in the range of at least 1 micrometer (μm) obtained byagglomeration of primary polymer comprising particles in the nanometerrange.

By the term “primary particle” as used is denoted a spherical polymercomprising particle in the nanometer range. Preferably the primaryparticle has a weight average particle size between 20 nm and 800 nm.

By the term “particle size” as used is denoted the volume averagediameter of a particle considered as spherical.

By the term “copolymer” as used is denoted that the polymer consists ofat least two different monomers.

By “multistage polymer” as used is denoted a polymer formed insequential fashion by a multi-stage polymerization process. Onepreferred process is a multi-stage emulsion polymerization process inwhich the first polymer is a first-stage polymer and the second polymeris a second-stage polymer, i.e., the second polymer is formed byemulsion polymerization in the presence of the first emulsion polymer.

By the term “(meth)acrylic” as used is denoted all kind of acrylic andmethacrylic monomers.

By the term “(meth)acrylic polymer” as used is denoted that the(meth)acrylic) polymer comprises essentially polymers comprising(meth)acrylic monomers that make up 50 wt % or more of the (meth)acrylicpolymer.

By the term “epoxy resin” as used is understood any organic compoundhaving at least two functional groups of oxirane type which can bepolymerized by ring opening.

By the term “(meth)acrylic resin” as used is understood adhesives basedon acrylic and methacrylic monomers.

By the term “masterbatch” as used is understood composition thatcomprises an additive in high concentration in a carrier material. Theadditive is dispersed in the carrier material.

By the term “impact modifier” as used is understood a material that onceincorporated in a polymeric material increases the impact resistance andtoughness of that polymeric material by phase micro domains of a rubberymaterial or rubber polymer.

By the term “rubber” as used is denoted to the thermodynamic state ofthe polymer above its glass transition.

By the term “rubber polymer” as used is denoted a polymer that has aglass transition temperature (Tg) below 0° C.

The liquid composition of the invention comprises at least threecomponents a) a (meth)acrylic polymer (P1), b) a multi stage polymer, c)a (meth)acrylic monomer (M1), wherein the multistage polymer to monomerratio by weight in the liquid composition is between 1/99 and 25/75, inthe liquid composition comprising the three compounds.

Preferably the multistage polymer to monomer (M1) ratio by weight in theliquid composition is between 2/98 and 24/76, more preferably between3/97 and 23/77, still more preferably between 4/96 and 22/78 andadvantageously between 5/95 and 20/80.

The dynamic viscosity of the liquid composition according to theinvention is in a range from 10 mPa*s to 1 000 000 mPa*s, preferablyfrom 10 mPa*s to 500 000 mPa*s and advantageously from 50 mPa*s to 300000 mPa*s. The viscosity of the liquid composition (sometimes alsocalled syrup) can be easily measured with a Rheometer with a shear ratebetween 0.1 s-1 and 100 s-1. The dynamic viscosity is measured at 25° C.If there is a shear thinning the viscosity is measured at a shear rateof 1 s-1.

With regard to the (meth)acrylic polymer (P1), it has a mass averagemolecular weight Mw of less than 100 000 g/mol, preferably less than 90000 g/mol, more preferably less than 80 000 g/mol, still more preferablyless than 70 000 g/mol, advantageously less than 60 000 g/mol, moreadvantageously less than 50 000 g/mol and still more advantageously lessthan 40 000 g/mol.

The (meth)acrylic polymer (P1), it has a mass average molecular weightMw above 2 000 g/mol, preferably above 3000 g/mol, more preferably above4000 g/mol, still more preferably above 5 000 g/mol, advantageouslyabove 6 000 g/mol, more advantageously above 6 500 g/mol and still moreadvantageously above 7 000 g/mol and most advantageously above 10 000g/mol.

The mass average molecular weight Mw of (meth)acrylic polymer (P1) isbetween 2 000 g/mol and 100 000 g/mol, preferable between 3 000 g/moland 90 000 g/mol and more preferably between 4 000 g/mol and 80 000g/mol advantageously between 5000 g/mol and 70 000 g/mol, moreadvantageously between 6 000 g/mol and 50 000 g/mol and mostadvantageously between 10 000 g/mol and 40 000 g/mol.

Preferably the (meth)acrylic polymer (P1) is a copolymer comprising(meth)acrylic monomers. More preferably the (meth)acrylic polymer (P1)is a (meth) acrylic polymer. Still more preferably the (meth)acrylicpolymer (P1) comprises at least 50 wt % monomers chosen from C1 to C12alkyl (meth)acrylates. Advantageously preferably the (meth)acrylicpolymer (P1) comprises at least 50 wt % of monomers chosen from C1 to C4alkyl methacrylate and C1 to C8 alkyl acrylate monomers and mixturesthereof.

Preferably the glass transition temperature Tg of the (meth)acrylicpolymer (P1) is between 30° C. and 150° C. The glass transitiontemperature of the (meth)acrylic polymer (P1) is more preferably between40° C. and 150° C., advantageously between 45° C. and 150° C. and moreadvantageously between 50° C. and 150° C.

Preferably the polymer (meth)acrylic polymer (P1) is not crosslinked.

Preferably the polymer (meth)acrylic polymer (P1) is not grafted on anyother polymer or polymers.

In a first preferred embodiment the (meth)acrylic polymer (P1) comprisesfrom 50 wt % to 100 wt % methyl methacrylate, preferably from 80 wt % to100 wt % methyl methacrylate, still more preferably from 80 wt % to 99.8wt % methyl methacrylate and from 0.2 wt % to 20 wt % of an C1 to C8alkyl acrylate monomer. Advantageously the C1 to C8 alkyl acrylatemonomer is chosen from methyl acrylate, ethyl acrylate or butylacrylate.

In a second preferred embodiment the (meth)acrylic polymer (P1)comprises between 0 wt % and 50 wt % of a functional monomer. Preferablythe (meth)acrylic polymer (P1) comprises between 0 wt % and 30 wt % ofthe functional monomer, more preferably between 1 wt % and 30 wt %,still more preferably between 2 wt % and 30 wt %, advantageously between3 wt % and 30 wt %, more advantageously between 5 wt % and 30 wt % andmost advantageously between 5 wt % and 30 wt %.

Preferably the functional monomer of the second preferred embodiment isa (meth)acrylic monomer. The functional monomer has the formula (1) or(2):

wherein in both formulas (1) and (2) R₁ is chosen from H or CH₃; and informula (1) Y is O, R₅ is H or an aliphatic or aromatic radical havingat least one atom that is not C or H; and in formula (2) Y is N and R₄and/or R₃ is H or an aliphatic or aromatic radical.

Preferably the functional monomer (1) or (2) is chosen from glycidyl(meth)acrylate, acrylic or methacrylic acid, the amides derived fromthese acids, such as, for example, dimethylacrylamide, 2-methoxyethylacrylate or methacrylate, 2-aminoethyl acrylates or methacrylates areoptionally quaternized, acrylate or methacrylate monomers comprising aphosphonate or phosphate group, alkyl imidazolidinone (meth) acrylates,polyethylene glycol (meth) acrylates. Preferably the polyethylene glycolgroup of polyethylene glycol (meth) acrylates has a molecular weightranging from 400 g/mol to 10 000 g/mol

The multistage polymer according to the invention has at least twostages that are different in its polymer composition.

The multistage polymer is preferably in form of polymer particlesconsidered as spherical particles. These particles are also called coreshell particles. The first stage forms the core, the second or allfollowing stages the respective shells. Such a multistage polymer whichis also called core/shell particle is preferred.

With regard to the polymeric particle according to the invention, whichis the primary particle, it has a weight average particle size(diameter) between 15 nm and 900 nm. Preferably the weight averageparticle size of the polymer is between 20 nm and 800 nm, morepreferably between, more preferably between 25 nm and 600 nm, still morepreferably between 30 nm and 550 nm, again still more preferably between35 nm and 500 nm, advantageously between 40 nm and 400 nm, even moreadvantageously between 75 nm and 350 nm and advantageously between 80 nmand 300 nm. The primary polymer particles can be agglomerated giving apolymer powder comprising either the multi stage polymer or the (meth)acrylic polymer (P1) and the multi stage polymer.

The polymer particle is obtained by a multistage process such as aprocess comprising two, three or more stages.

The polymer particle has a multilayer structure comprising at least onelayer (A) comprising a polymer (A1) having a glass transitiontemperature below 0° C. and another layer (B) comprising a polymer (B1)having a glass transition temperature over 30° C.

In a first preferred embodiment the polymer (B1) having a glasstransition temperature of at least 30° C. is the external layer of thepolymer particle having the multilayer structure.

In a second preferred embodiment the polymer (B1) having a glasstransition temperature of at least 30° C. is an intermediate layer ofthe polymer particle having the multilayer structure, before themultistage polymer is brought into contact with the monomer (M1).

Preferably the stage (A) is the first stage and the stage (B) comprisingpolymer (B1) is grafted on stage (A) comprising polymer (A1) or anotherintermediate layer. By first stage is meant that the stage (A)comprising polymer (A1) is made before the stage (B) comprising polymer(B1).

The polymer (A1) having a glass transition temperature below 0° C. inthe layer (A) is never made during the last stage of the multistageprocess. This means that the polymer (A1) is never in the external layerof the particle with the multilayer structure. The polymer (A1) having aglass transition temperature below 0° C. in the layer (A) is either inthe core of the polymer particle or one of the inner layers.

Preferably the polymer (A1) having a glass transition temperature below0° C. in the layer (A) is made in the first stage of the multistageprocess forming the core for the polymer particle having the multilayerstructure and/or before the polymer (B1) having a glass transitiontemperature over 60° C. Preferably the polymer (A1) is having a glasstransition temperature below −5° C., more preferably below −15° C.,advantageously below −25° C.

In a first preferred embodiment the polymer (B1) having a glasstransition temperature over 60° C. is made in the last stage of themultistage process forming the external layer of the polymer particlehaving the multilayer structure.

In a second preferred embodiment the polymer (B1) having a glasstransition temperature of at least 30° C. is an intermediate layer ofthe polymer particle having the multilayer structure, is made in a stageafter the stage for forming the polymer (A1) of the multistage process.

There could be additional intermediate layer or layers obtained by anintermediate stage or intermediate stages.

The glass transition temperature Tg of the respective polymers can beestimated for example by dynamic methods as thermo mechanical analysis.

In order to obtain a sample of the respective polymers (A1) and (B1)they can be prepared alone, and not by a multistage process, forestimating and measuring more easily the glass transition temperature Tgindividually of the respective polymers of the respective stages.

With regard to the polymer (A1), in a first embodiment it is a (meth)acrylic polymer comprising at least 50 wt % of monomers from alkylacrylates.

More preferably the polymer (A1) comprises a comonomer or comonomerswhich are copolymerizable with alkyl acrylate, as long as polymer (A1)is having a glass transition temperature of less than 0° C.

The comonomer or comonomers in polymer (A1) are preferably chosen from(meth)acrylic monomers and/or vinyl monomers.

The (meth)acrylic comonomer in polymer (A1) comprises monomers chosenfrom C1 to C12 alkyl (meth)acrylates. Still more preferably(meth)acrylic comonomer in polymer (A1) comprises monomers of C1 to C4alkyl methacrylate and/or C1 to C8 alkyl acrylate monomers.

Most preferably the acrylic or methacrylic comonomers of the polymer(A1) are chosen from methyl acrylate, propyl acrylate, isopropylacrylate, butyl acrylate, tert-butyl acrylate, methyl methacrylate,ethyl methacrylate, butyl methacrylate and mixtures thereof, as long aspolymer (A1) is having a glass transition temperature of less than 0° C.

Preferably the polymer (A1) is crosslinked. This means that acrosslinker is added to the other monomer or monomers. A crosslinkercomprises at least two groups that can be polymerized.

In one specific embodiment polymer (A1) is a homopolymer of butylacrylate.

In another specific embodiment polymer (A1) is a copolymer of butylacrylate and at least one crosslinker. The crosslinker presents lessthan 5 wt % of this copolymer.

More preferably the glass transition temperature Tg of the polymer (A1)of the first embodiment is between −100° C. and 0° C., even morepreferably between −100° C. and −5° C., advantageously between −90° C.and −15° C. and more advantageously between −90° C. and −25° C.

With regard to the polymer (A1), in a second embodiment the polymer (A1)is a silicone rubber based polymer. The silicone rubber for example ispolydimethyl siloxane. More preferably the glass transition temperatureTg of the polymer (A1) of the second embodiment is between −150° C. and0° C., even more preferably between −145° C. and −5° C., advantageouslybetween −140° C. and −15° C. and more advantageously between −135° C.and −25° C.

With regard to the polymer (A1), in a third embodiment the polymer (A1)having a glass transition temperature below 0° C. comprises at least 50wt % of polymeric units coming from isoprene or butadiene and the stage(A) is the most inner layer of the polymer particle having themultilayer structure. In other words the stage (A) comprising thepolymer (A1) is the core of the polymer particle.

By way of example, the polymer (A1) of the core of the secondembodiment, mention may be made of isoprene homopolymers or butadienehomopolymers, isoprene-butadiene copolymers, copolymers of isoprene withat most 98 wt % of a vinyl monomer and copolymers of butadiene with atmost 98 wt % of a vinyl monomer. The vinyl monomer may be styrene, analkylstyrene, acrylonitrile, an alkyl (meth)acrylate, or butadiene orisoprene. In one embodiment the core is a butadiene homopolymer.

More preferably the glass transition temperature Tg of the polymer (A1)of the third embodiment comprising at least 50 wt % of polymeric unitscoming from isoprene or butadiene is between −100° C. and 0° C., evenmore preferably between −100° C. and −5° C., advantageously between −90°C. and −15° C. and even more advantageously between −90° C. and −25° C.

With regard to the polymer (B1), mention may be made of homopolymers andcopolymers comprising monomers with double bonds and/or vinyl monomers.Preferably the polymer (B1) is a (meth) acrylic polymer.

Preferably the polymer (B1) comprises at least 70 wt % monomers chosenfrom C1 to C12 alkyl (meth)acrylates. Still more preferably the polymer(B1) comprises at least 80 wt % of monomers C1 to C4 alkyl methacrylateand/or C1 to C8 alkyl acrylate monomers.

The polymer (B1) can be crosslinked.

Most preferably the acrylic or methacrylic monomers of the polymer (B1)are chosen from methyl acrylate, ethyl acrylate, butyl acrylate, methylmethacrylate, ethyl methacrylate, butyl methacrylate and mixturesthereof, as long as polymer (B1) is having a glass transitiontemperature of at least 30° C.

Advantageously the polymer (B1) comprises at least 50 wt %, moreadvantageously at least 60 wt % and even more advantageously at least 70wt % of monomer units coming from methyl methacrylate.

Preferably the glass transition temperature Tg of the polymer (B1) isbetween 30° C. and 150° C. The glass transition temperature of thepolymer (B1) is more preferably between 50° C. and 150° C., still morepreferably between 70° C. and 150° C., advantageously between 90° C. and150° C. and more advantageously between 90° C. and 130° C.

In another embodiment the multi stage polymer as described previously,has an additional stage, which is the (meth)acrylic polymer (P1). Theprimary polymer particle according to this embodiment of the inventionhas a multilayer structure comprising at least one stage (A) comprisinga polymer (A1) having a glass transition temperature below 0° C., atleast one stage (B) comprising a polymer (B1) having a glass transitiontemperature over 30° C. and at least one stage (P) comprising the(meth)acrylic polymer (P1) having a glass transition temperature between30° C. and 150° C.

Preferably the (meth)acrylic polymer (P1) is not grafted on any of thepolymers (A1) or (B1).

With regard to the process for manufacturing the multistage polymeraccording to the invention it comprises the steps of

-   -   a) polymerizing by emulsion polymerization of a monomer or        monomer mixture (A_(m)) to obtain at least one layer (A)        comprising polymer (A1) having a glass transition temperature of        less than 0° C.    -   b) polymerizing by emulsion polymerization of a monomer or        monomer mixture (B_(m)) to obtain layer (B) comprising a polymer        (B1) having a glass transition temperature of at least 30° C.        the monomer or monomer mixture (A_(m)) and the monomer or        monomer mixture (B_(m)) are chosen from monomers according to        the composition for polymer (A1) and polymer (B1) given earlier.

Preferably the step a) is made before step b). More preferably step b)is performed in presence of the polymer (A1) obtained in step a), ifthere are only two stages.

Advantageously the process for manufacturing the multistage polymercomposition according to the invention is a multistep process comprisesthe steps one after the other of

-   -   a) polymerizing by emulsion polymerization of a monomer or        monomer mixture (A_(m)) to obtain one layer (A) comprising        polymer (A1) having a glass transition temperature of less than        0° C.    -   b) polymerizing by emulsion polymerization of a monomer or        monomer mixture (B_(m)) to obtain layer (B) comprising a polymer        (B1) having a glass transition temperature of at least 30° C.

The respective monomers or monomer mixtures (A_(m)) and (B_(m)) forforming the layers (A) and (B) respectively comprising the polymers (A1)and (B1) respectively and the characteristics of the respective polymers(A1) and (B1) are the same as defined before.

The process for manufacturing the multistage polymer can compriseadditional steps for additional stages between the steps a) and b).

The process for manufacturing the multistage polymer can also compriseadditional steps for additional stages before the steps a) and b). Aseed could be used for polymerizing by emulsion polymerization themonomer or monomers mixture (A_(m)) to obtain the layer (A) comprisingpolymer (A1) having a glass transition temperature of less than 0° C.The seed is preferably a thermoplastic polymer having a glass transitiontemperature of at least 20° C.

The multistage polymer is obtained as an aqueous dispersion of thepolymer particles. The solid content of the dispersion is between 10 wt% and 65 wt %.

With regard to the process for manufacturing the (meth)acrylic polymer(P1) according to the invention is comprises the step of polymerizingthe respective (meth)acrylic monomers (P1_(m)). The respective(meth)acrylic monomers (P1_(m)) are the same as defined before for the(meth)acrylic polymer (P1) and two preferred embodiments the(meth)acrylic polymer (P1).

The (meth)acrylic homo or copolymer (P1) could be made in batch orsemi-continuous process:

-   -   for the batch process, the mixture of monomers is introduced in        one shot just before or after introduction of one or part of the        initiator system    -   for the semi-continuous process, the monomer mixture is added in        multiple shots or continuously in parallel to the initiator        addition (the initiator is also added in multiple shots or        continuously) during a defined period of addition which could be        in the range 30 to 500 min.

The process for preparing the polymer composition comprising the (meth)acrylic polymer (P1) and the multi stage polymer has two preferredembodiments.

In a first preferred embodiment of the process, the (meth) acrylicpolymer (P1) is polymerized in the presence of the multistage polymer.The (meth) acrylic polymer (P1) is made as an additional stage of themultistage polymer.

In a second preferred embodiment of the process, the (meth) acrylicpolymer (P1) is polymerized apart and mixed or blended with themultistage polymer.

With regard to the process according to the first preferred embodimentfor preparing the polymer composition comprising the (meth) acrylicpolymer (P1) and the multi stage polymer, it comprises the steps of

-   -   a) polymerizing by emulsion polymerization of a monomer or        monomer mixture (A_(m)) to obtain one layer in stage (A)        comprising polymer (A1) having a glass transition temperature of        less than 0° C.    -   b) polymerizing by emulsion polymerization of a monomer or        monomer mixture (B_(m)) to obtain layer in stage (B) comprising        a polymer (B1) having a glass transition temperature of at least        30° C.    -   c) polymerizing by emulsion polymerization of a monomer or        monomer mixture (P1_(m)) to obtain a layer in this additional        stage comprising the (meth) acrylic polymer (P1) having a glass        transition temperature of at least 30° C.        characterized that the (meth) acrylic polymer (P1) has a mass        average molecular weight Mw of less than 100 000 g/mol.

Preferably the step a) is made before step b).

More preferably step b) is performed in presence of the polymer (A1)obtained in step a).

Advantageously the method for manufacturing the polymer compositioncomprising the (meth) acrylic polymer (P1) and the multi stage polymeris a multistep process and comprises the steps one after the other of

-   -   a) polymerizing by emulsion polymerization of a monomer or        monomer mixture (A_(m)) to obtain one layer in stage (A)        comprising polymer (A1) having a glass transition temperature of        less than 0° C.        -   b) polymerizing by emulsion polymerization of a monomer or            monomer mixture (B_(m)) to obtain layer in stage (B)            comprising a polymer (B1) having a glass transition            temperature of at least 30° C.        -   c) polymerizing by emulsion polymerization of a monomer or            monomer mixture (P1_(m)) to obtain a layer in this            additional stage comprising the (meth) acrylic polymer (P1)            having a glass transition temperature of at least 30° C.            characterized that the (meth) acrylic polymer (P1) has a            mass average molecular weight Mw of less than 100 000 g/mol.

The respective monomers or monomer mixtures (A_(m)), (B_(m)) and(P1_(m)) for forming the layers (A), (B) and additional stagerespectively comprising the polymers (A1), (B1) and (P1) respectively,are the same as defined before. The characteristics of the polymers(A1), (B1) and (P1) respectively, are the same as defined before.

Preferably the method for manufacturing the polymer compositioncomprising the (meth) acrylic polymer (P1) and the multi stage polymercomprises the additional step d) of recovering of this polymercomposition.

By recovering is meant partial or separation between the aqueous andsolid phase, latter comprises the polymer composition.

More preferably according to the invention the recovering of the polymercomposition is made by coagulation or by spray-drying.

Spray drying is the preferred method for the recovering and/or dryingfor the manufacturing method for a polymer powder composition if thepolymer (A1) having a glass transition temperature below 0° C. comprisesat least 50 wt % of polymeric units coming from alkyl acrylate and thestage (A) is the most inner layer of the polymer particle having themultilayer structure.

Coagulation is the preferred method for the recovering and/or drying forthe manufacturing method for a polymer powder composition according tothe present invention if the polymer (A1) having a glass transitiontemperature below 10° C. comprises at least 50 wt % of polymeric unitscoming from isoprene or butadiene and the stage (A) is the most innerlayer of the polymer particle having the multilayer structure.

The method for manufacturing the polymer composition according to theinvention can comprise optionally the additional step e) of drying ofthe polymer composition.

Preferably the drying step e) is made if the step d) of recovering ofthe polymer composition is made by coagulation.

Preferably after the drying step an e) the polymer composition comprisesless than 3 wt %, more preferably less than 1.5 wt % advantageously lessthan 1% of humidity or water.

The humidity of a polymer composition can be measure with a thermobalance.

The drying of the polymer can be made in an oven or vacuum oven withheating of the composition for 48 hours at 50° C.

With regard to the process according to the second preferred embodimentfor preparing the polymer composition comprising the (meth) acrylicpolymer (P1) and the multi stage polymer, it comprises the steps of

-   -   a) mixing of the (meth) acrylic polymer (P1) and the multi stage        polymer    -   b) recovering the obtained mixture of previous step in form of a        polymer powder        wherein the (meth) acrylic polymer (P1) and the multi stage        polymer in step a) are in form of a dispersion in aqueous phase.

The quantities of the aqueous dispersion of the (meth) acrylic polymer(P1) and the aqueous dispersion of the multi stage polymer are chosen ina way that the weight ratio of the multi stage polymer based on solidpart only in the obtained mixture is at least 5 wt %, preferably atleast 10 wt %, more preferably at least 20 wt % and advantageously atleast 50 wt %.

The quantities of the aqueous dispersion of the (meth) acrylic polymer(P1) and the aqueous dispersion of the multi stage polymer are chosen ina way that the weight ratio of the multi stage polymer based on solidpart only in the obtained mixture is at most 99 wt %, preferably at most95 wt % and more preferably at most 90 wt %.

The quantities of the aqueous dispersion of the (meth) acrylic polymer(P1) and the aqueous dispersion of the multi stage polymer are chosen ina way that the weight ratio of the multi stage polymer based on solidpart only in the obtained mixture is between 5 wt % and 99 wt %,preferably between 10 wt % and 95 wt % and more preferably between 20 wt% and 90 wt %.

The recovering step b) of the process for manufacturing the polymercomposition comprising the (meth) acrylic polymer (P1) and the multistage polymer, is preferably made by coagulation or by spray drying.

The process for manufacturing the polymer composition comprising the(meth) acrylic polymer (P1) and the multi stage polymer can optionallycomprise the additional step c) for drying the polymer composition.

By dry is meant that the polymer composition according to the presentinvention comprises less than 3 wt % humidity and preferably less than1.5 wt % humidity and more preferably less than 1.2 wt % humidity.

The humidity can be measured by a thermo balance that heats the polymercomposition and measures the weight loss.

The process for manufacturing the polymer composition comprising the(meth) acrylic polymer (P1) and the multi stage polymer yieldspreferably to a polymer powder. The polymer powder of the invention isin form of particles. A polymer powder particle comprises agglomeratedprimary polymer particles made by multistage process and the (meth)acrylic polymer (P1).

With regard to the polymer powder comprising the (meth) acrylic polymer(P1) and the multi stage polymer according to the two embodiments of theprocess of preparation, it has a volume median particle size D50 between1 μm and 500 μm. Preferably the volume median particle size of thepolymer powder is between 10 μm and 400 μm, more preferably between 15μm and 350 μm and advantageously between 20 μm and 300 μm.

The D10 of the particle size distribution in volume is at least 7 μm andpreferably 10 μm.

The D90 of the particle size distribution in volume is at most 950 μmand preferably 500 μm, more preferably at most 400 μm.

The weight ratio r of the (meth) acrylic polymer (P1) in relation to themulti stage polymer is at least 5 wt %, more preferably at least 7 wt %and still more preferably at least 10 wt %.

According to the invention the ratio r of the (meth) acrylic polymer(P1) in relation to the multi stage polymer is at most 95 w %.

Preferably the weight ratio of the (meth) acrylic polymer (P1) inrelation to the multi stage polymer is between 5 wt % and 95 wt % andpreferably between 10 wt % and 90 wt %.

With regard to the (meth)acrylic monomer (M1) it is a liquid monomer atleast in the temperature range between 0° C. and 60° C. The(meth)acrylic monomer (M1) comprises one carbon C═C double bond.

The (meth)acrylic monomer (M1) according to the invention is a monomerthat is a solvent for the (meth) acrylic polymer (P1). In other word the(meth) acrylic polymer (P1) is soluble in the (meth)acrylic monomer(M1).

Soluble means that in a certain time the (meth) acrylic polymer (P1) incontact the thermodynamically compatible (meth)acrylic monomer (M1) isdissolved and a solution of the (meth) acrylic polymer (P1) in the(meth)acrylic monomer (M1) is obtained.

The solubility of the (meth) acrylic polymer (P1) in the (meth)acrylicmonomer (M1) can be simply tested by mixing under agitation at 25° C.the two compounds. For one skilled in the art the solvents includingmonomers as (meth)acrylic monomer (M1) for a large number of polymersare known. On the other hand solubility parameter values are given for alarge number of polymer and solvents, latter including a large number ofmonomers for example in Polymer Handbook (4^(th) edition) Ed. J.Brandrup, E. H. Immergut and E. A. Grulke; Pub.: John Wiley and SonsInc. 1999, Chapter “Solubility Parameter Value” by Eric A. Gulke VII/675to VII/714.

The (meth)acrylic monomer (M1) is preferably chosen from (meth)acrylicmonomers and mixtures thereof. If the (meth)acrylic monomer (M1) is amixture of several monomers, the (meth) acrylic polymer (P1) is solublein the mixture comprising the (meth)acrylic monomer(s) (M1).

The (meth)acrylic monomer (M1) is more preferably chosen from acrylicacid, methacrylic acid, alkyl acrylic monomers, alkyl methacrylicmonomers and mixtures thereof.

Still more preferably the (meth)acrylic monomer (M1) is chosen fromacrylic acid, methacrylic acid, alkyl acrylic monomers, alkylmethacrylic monomers and mixtures thereof, the alkyl group having from 1to 22 carbons, either linear, branched or cyclic; preferably the alkylgroup having from 1 to 12 carbons, either linear, branched or cyclic.

Advantageously the (meth)acrylic monomer (M1) is chosen from methylmethacrylate, ethyl methacrylate, methyl acrylate, ethyl acrylate,methacrylic acid, acrylic acid, n-butyl acrylate, iso-butyl acrylate,n-butyl methacrylate, iso-butyl methacrylate, cyclohexyl acrylate,cyclohexyl methacrylate, isobornyl acrylate, isobornyl methacrylate andmixtures thereof.

More advantageously the (meth)acrylic monomer (M1) is chosen from methylmethacrylate, isobornyl acrylate or acrylic acid and mixtures thereof.

In a first most advantageously embodiment at least 50 wt %, preferablyat least 60 wt % of the (meth)acrylic monomer (M1) is methylmethacrylate.

In a second most advantageously at least 50 wt %, preferably at least 60wt %, more preferably at least 70 wt % and advantageously at least 80 wt% and even more advantageously 90 wt % of the (meth)acrylic monomer (M1)is a mixture of methyl methacrylate with isobornyl acrylate and/oracrylic acid.

The liquid composition of the present invention that is less viscousthan a composition not comprising the (meth)acrylic polymer (P1).

The liquid composition of the present invention can be used to prepare abetter dispersed multistage polymer instead of a composition notcomprising the (meth)acrylic polymer (P1).

With regard to the process for manufacturing the liquid composition iscomprises the steps of

-   -   a) preparing a composition comprising a (meth) acrylic polymer        (P1) and a multi stage polymer    -   b) mixing the composition of previous step with a (meth)acrylic        monomer (M1)        wherein the multistage polymer to (meth)acrylic monomer (M1)        ratio by weight in the liquid composition is between 1/99 and        25/75.

Preferably the (meth) acrylic polymer (P1) has a mass average molecularweight Mw of less than 100 000 g/mol. The (meth) acrylic polymer (P1) isthe same as defined before.

The composition comprising the (meth) acrylic polymer (P1) and a multistage polymer can be in form of the polymer powder as obtained by thetwo preferred embodiments of preparation.

The process yields to a liquid composition that is less viscous than acomposition not comprising the (meth)acrylic polymer (P1).

The process yields to a liquid composition that possesses a betterdispersion of the multistage polymer than a composition not comprisingthe (meth)acrylic polymer (P1).

The agglomerated polymer powder is better dispersed in the solvent whenthe (meth)acrylic polymer (P1) is present.

The process of the invention for manufacturing the liquid compositioncan be used to prepare a better dispersed multistage polymer than acomposition not comprising the (meth)acrylic polymer (P1).

An additional aspect of the invention is that the liquid compositioncomprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer (M1) ratio by weight        in the liquid composition is between 1/99 and 25/75, can be used        to prepare a better dispersion of the multistage polymer in the        monomer (M1) than a composition not comprising the(meth)acrylic        polymer (P1).

Another additional aspect of the invention is that the liquidcomposition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer ratio by weight in the        liquid composition is between 1/99 and 25/75, can be used for        the preparation of the impact modified polymers, by polymerizing        the (meth)acrylic monomer (M1).

The liquid composition according to the invention can also be mixed withother monomers and polymers that are not part of the liquid compositionbefore polymerization. The liquid composition according to the inventioncan be used as a liquid masterbatch.

The multistage polymer is better distributed in the polymer matrix afterpolymerization instead than using a composition not comprising the(meth)acrylic polymer (P1).

Another additional aspect of the invention is that the liquidcomposition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer ratio by weight in the        liquid composition is between 1/99 and 25/75, can be used as an        impregnation liquid (meth) acrylic syrup, preferably for a        fibrous substrate.

Another additional aspect of the invention is process for manufacturinga liquid composition comprising the steps of

-   -   a) preparing a composition comprising a the (meth) acrylic        polymer (P1) and a multi stage polymer    -   b) mixing the composition of previous step with a (meth)acrylic        monomer (M1)        wherein the multistage polymer to monomer (M1) ratio by weight        in the liquid composition is between 1/99 and 25/75, for an        impregnation liquid in form of a (meth) acrylic syrup,        preferably an impregnation liquid for a fibrous substrate.

Another additional aspect of the invention relates to an impregnationprocess for impregnating a fibrous substrate, wherein said fibroussubstrate comprises long fibres and said process comprises a step ofimpregnating said fibrous substrate with a liquid compositioncomprising:

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multistage polymer and    -   c) a (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer ratio by weight in the        liquid composition is between 1/99 and 25/75.

Another additional aspect of the invention relates to the use of aliquid composition comprising

-   -   a) a (meth)acrylic polymer (P1),    -   b) a multi stage polymer and    -   c) a (meth)acrylic monomer (M1)        wherein the multistage polymer to monomer ratio by weight in the        liquid composition is between 1/99 and 25/75, in an impregnation        process for impregnating a fibrous substrate.

Preferably said fibrous substrate comprises long fibres.

The liquid composition according to the invention can be used as aliquid masterbatch for the use as an impregnation liquid (meth) acrylicsyrup or in an impregnation process for impregnating a fibroussubstrate. The liquid composition is diluted with another monomer.

With regard to the fibrous substrate, one can mention fabrics, felts ornonwovens that may be in the form of strips, laps, braids, locks orpieces. The fibrous material can have different forms and dimensionseither one dimensional, two dimensional or three dimensional. A fibroussubstrate comprises an assembly of one or more fibres. When the fibresare continuous, their assembly forms fabrics.

The one dimensional form is linear long fibres. The fibers may bediscontinuous or continuous. The fibers may be arranged randomly or as acontinuous filament parallel to each other. A fiber is defined by itsaspect ratio, which is the ratio between length and diameter of thefiber. The fibers used in the present invention are long fibers orcontinuous fibers. The fibers have an aspect ratio of at least 1000,preferably at least 1500, more preferably at least 2000, advantageouslyat least 3000 and most advantageously at least 5000.

The two dimensional form are fibrous mats or non woven reinforcements orwoven roving or bundles of fibers, which can also be braided.

The three dimensional form are for example stacked or folded fibrousmats or non woven reinforcements or bundles of fibers or mixturesthereof, an assembly of the two dimensional form in the third dimension.

The origins of the fibrous material can be a natural or a synthetic one.As natural material one can mention vegetable fibers, wood fibers,animal fibers or mineral fibers.

Natural fibers are for example sisal, jute, hemp, flax, cotton, coconutfibers, and banana fibers. Animal fibers are for example wool or hair.

As synthetic material one can mention polymeric fibers chosen fromfibers of thermosetting polymers, from thermoplastic polymers or theirmixtures.

The polymeric fibers can be made of polyamide (aliphatic or aromatic),polyester, polyvinylalcohol, polyolefins, polyurethanes,polyvinylchloride, polyethylene, unsatured polysters, epoxy resins andvinylesters.

The mineral fibers can also be chosen from glass fibers especially oftype E, R or S2, carbon fibers, boron fibers or silica fibers.

The fibrous substrate of the present invention is chosen from vegetablefibers, wood fibers, animal fibers, mineral fibers, synthetic polymericfibers, glass fibers, carbon fibers or mixtures thereof.

Preferably the fibrous substrate is chosen from mineral fibers.

[Methods of Evaluation]

Viscosity Measurements

The viscosity is measured with a MCR 301 rheometer from Anton Paar.Couette geometry is used. Temperature is 25° C. and with a shear ratefrom 0.1 s-1 to 100 s-1.

Glass Transition Temperature

The glass transitions (Tg) of the polymers are measured with equipmentable to realize a thermo mechanical analysis. A RDAII “RHEOMETRICSDYNAMIC ANALYSER” proposed by the Rheometrics Company has been used. Thethermo mechanical analysis measures precisely the visco-elastics changesof a sample in function of the temperature, the strain or thedeformation applied. The apparatus records continuously, the sampledeformation, keeping the stain fixed, during a controlled program oftemperature variation. The results are obtained by drawing, in functionof the temperature, the elastic modulus (G′), the loss modulus and thetan delta. The Tg is higher temperature value read in the tan deltacurve, when the derived of tan delta is equal to zero.

Molecular Weight

The mass average molecular weight (Mw) of the polymers is measured withby size exclusion chromatography (SEC).

Particle Size Analysis

The particle size of the primary particles after the multistagepolymerization is measured with a Zetasizer.

The particle size of the polymer powder after recovering is measuredwith Malvern Mastersizer 3000 from MALVERN.

For the estimation of weight average powder particle size, particle sizedistribution and ratio of fine particles a Malvern Mastersizer 3000apparatus with a 300 mm lenses, measuring a range from 0.5-880 μm isused.

EXAMPLES

Synthesis of multistage polymer (core-shell particles) is made accordingto the example of sample 1 of WO2012/038441 in order to obtain amultistage polymer. The multistage polymer CS1 is obtained. It comprisesa stage (A) comprising a polymer (A1) having a glass transitiontemperature of less than 0° (essentially made of butyl acrylate) and astage (B) comprising a polymer (B1) having a glass transitiontemperature of at least 30° C. (essentially made of methylmethacrylate). The multistage polymer CS1 is kept as an aqueousdispersion for further use.

Synthesis of a (meth)acrylic polymer type (P1) is made according to twoembodiments: first the (meth) acrylic polymer (P1) is polymerized in thepresence of the multistage polymer CS1. The (meth) acrylic polymer (P1)is made as an additional stage of the multistage polymer CS. And in asecond embodiment the (meth) acrylic polymer (P1) is polymerized apartand mixed or blended with the multistage polymer after the end ofpolymerization of the (meth) acrylic polymer (P1).

Comparative Example 1

The multistage polymer CS1 is mixed with methyl methacrylate (MMA) at20° C. under agitation so that 15 wt % of CS1 are in the liquidcomposition relatively to the MMA.

Example 1

The (meth) acrylic polymer (P1) is made as an additional stage on themultistage polymer CS1. The mass average molecular weight of the(meth)acrylic polymer P1 is M_(w)=28 000 g/mol.

The final polymer composition was then recovered, the polymercomposition being dried by spray drying. The obtained polymercomposition is mixed with methyl methacrylate (MMA) at 20° C. underagitation so that 15 wt % of CS1 relatively to MMA are in the liquidcomposition comprising MMA, (meth)acrylic polymer (P1) and multistagepolymer CS1.

Example 2

The (meth) acrylic polymer (P1) is polymerized apart and mixed orblended with the multistage polymer CS1. Synthesis of the (meth) acrylicpolymer (P1): semi continuous process: charged into a reactor, withstirring, were 1700 g of de-ionized water, 0.01 g of FeSO4 and 0.032 gof ethylenediaminetetraacetic acid, sodium salt (dissolved in 10 g ofde-ionized water), 3.15 g of sodium formaldehydesulfoxylate dissolved if110 g of de-ionized water and 21.33 g of emulsifier potassium salt ofbeef tallow fatty acid (dissolved in 139.44 g of water), and the mixturewas stirred until complete dissolution. Three vacuum-nitrogen purgeswere carried out in succession and the reactor left under a slightvacuum. The reactor was then heated. At the same time, a mixturecomprising 960.03 g of methyl methacrylate, 106.67 g ofdimethylacrylamide and 10.67 g of n-octyl mercaptan wasnitrogen-degassed for 30 minutes. The reactor is heated at 63° C. andmaintained at that temperature. Next, the monomers mixture wasintroduced into the reactor in 180 min using a pump. In parallel, asolution of 5.33 g of ter-butyl hydroperoxide (dissolved in 100 g ofde-ionized water) is introduced (same addition time). The lines wasrinsed with 50 g and 20 g of water. Then the reaction mixture was heatedat a temperature of 80° C. and the polymerization was then left tocompletion for 60 minutes after the end of the monomers addition. Thereactor was cooled down to 30° C. The obtained solid content is 34.2%.The mass average molecular weight of the (meth)acrylic polymer P1 isM_(w)=28 000 g/mol.

The aqueous dispersion of the multistage polymer CS1 and the (meth)acrylic polymer (P1) are mixed in quantities that the weight ratio basedon solid polymer between the (meth) acrylic polymer (P1) and themultistage polymer CS1 is 15/85. The mixture was recuperated as a powerby spray drying.

The obtained mixture of is mixed with methyl methacrylate at 20° C.under agitation so that 15 wt % of CS1 relatively to MMA are in theliquid composition comprising MMA, (meth)acrylic polymer (P1) andmultistage polymer CS1.

Example 3

Example 2 is repeated but the weight ratio based on solid polymerbetween the (meth) acrylic polymer (P1) and the multistage polymer CS1is 25/75.

The viscosity of the respective liquid compositions is measured.

TABLE 1 viscosity results Solid content Solid of polymers content CS1Viscosity (CS1 + P1) in in [Pa * s] at composition composition ExampleSample 0.1 s⁻¹ [wt %] [wt %] Comparative Liquid 1160 15 15 example 1composition of MMA with 15% CS1 Example 1 Liquid 289 16.87 15composition of MMA with CS1 and additional shell polymer Example 2Liquid 123 17.64 15 composition of MMA with blend of P1 and CS115/85 wtratio Example 3 Liquid 87 20 15 composition of MMA with blend of P1 andCS1 at 25/75 wt ratio

As shown in table 1 the global solid content of polymer increases whilethe ratio of the core-shell polymer stays constant at 15 wt % relativelyto the monomer, but the dynamic viscosity of the composition decreases.

The core shell particles are more efficiently dispersed having a lowereffective volume in the liquid composition, when the methacrylic polymeris present.

A glass fibre matt is impregnated with by an infusion process with theliquid compositions according to the examples, more easily and fasterthan with the composition according to the comparative example.

1. A liquid composition comprising a) a (meth) acrylic polymer (P1), b)a multistage polymer and c) a (meth)acrylic monomer (M1) wherein themultistage polymer to monomer ratio by weight in the liquid compositionis between 1/99 and 25/75.
 2. The composition according to claim 1,characterized that the (meth) acrylic polymer (P1) has a mass averagemolecular weight Mw of less than 100 000 g/mol.
 3. The compositionaccording to claim 1, characterized that the (meth) acrylic polymer (P1)has a mass average molecular weight Mw of less than 50 000 g/mol.
 4. Thecomposition according to claim 1, characterized that the (meth) acrylicpolymer (P1) has a mass average molecular weight Mw above 5 000 g/mol.5. The composition according to claim 1, characterized that the (meth)acrylic polymer (P1) has a mass average molecular weight Mw between 5000 g/mol and 70 000 g/mol, more advantageously between 6 000 g/mol and50 000 g/mol.
 6. The composition of claim 1 wherein the multistagepolymer to (meth)acrylic monomer ratio by weight in the liquidcomposition is between 2/98 and 24/76.
 7. The composition according toclaim 1, characterized that the (meth) acrylic polymer (P1) is solublein the (meth)acrylic monomer (M1).
 8. The composition according to claim1, characterized that the monomer (M1) is selected from the groupconsisting of acrylic acid, methacrylic acid, alkyl acrylic monomers,alkyl methacrylic monomers and mixtures thereof, the alkyl group havingfrom 1 to 22 carbons, either linear, branched or cyclic.
 9. Thecomposition according to claim 1, characterized that the monomer (M1) isselected from the group consisting of methyl methacrylate, ethylmethacrylate, methyl acrylate, ethyl acrylate, methacrylic acid, acrylicacid, n-butyl acrylate, iso-butyl acrylate, n-butyl methacrylate,iso-butyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate,isobornyl acrylate, isobornyl methacrylate and mixtures thereof.
 10. Thecomposition according to claim 1, characterized that the multi stagepolymer comprises a) one stage (A) comprising a polymer (A1) having aglass transition temperature of less than 0° C. b), one stage (B)comprising a polymer (B1) having a glass transition temperature of atleast 30° C.
 11. The composition according to claim 10, characterizedthat the stage (A) is the first stage and that stage (B) comprisingpolymer (B1) is grafted on stage (A) comprising polymer (A1).
 12. Thecomposition according to claim 10 characterized that the polymers (A1)and (B1) are acrylic or methacrylic polymers.
 13. The compositionaccording to claim 10 characterized that the polymer (A1) comprises atleast 50 wt % of polymeric units coming from isoprene or butadiene. 14.The composition according to claim 1 characterized that the (meth)acrylic polymer (P1) comprises at least 50 wt % monomers chosen from C1to C12 alkyl (meth)acrylates.
 15. The composition according to claim 1characterized that the (meth) acrylic polymer (P1) comprises from 50 wt% to 100 wt % methyl methacrylate and from 0.2 wt % to 20 wt % of an C1to C8 alkyl acrylate monomer.
 16. The composition according to claim 1characterized that the (meth) acrylic polymer (P1) comprises between 0wt % and 50 wt % of a functional monomer.
 17. The composition accordingto claim 1 characterized that the (meth) acrylic polymer (P1) comprisesbetween 1 wt % and 30 wt % of a functional monomer.
 18. The compositionaccording to claim 16, characterized that the functional monomer isselected from the group consisting of glycidyl (meth)acrylate, acrylicor methacrylic acid, amides derived from acrylic or methacrylic acid,2-methoxyethyl acrylate or methacrylate, 2-aminoethyl acrylates ormethacrylates, acrylate or methacrylate monomers comprising aphosphonate or phosphate group, alkyl imidazolidinone (meth) acrylates,and polyethylene glycol (meth) acrylates.
 19. A process formanufacturing a liquid composition according to any of claim 1comprising the steps of a) preparing a composition comprising a (meth)acrylic polymer (P1) and a multi stage polymer b) mixing the compositionof previous step with a (meth)acrylic monomer (M1) wherein themultistage polymer to monomer ratio in the liquid composition is between1/99 and 25/75.
 20. The process according to claim 19, characterizedthat the (meth) acrylic polymer (P1) has a mass average molecular weightMw of less than 100 000 g/mol.
 21. The process according to claim 19,characterized that the (meth) acrylic polymer (P1) has a mass averagemolecular weight Mw of has a mass average molecular weight Mw between 5000 g/mol and 70 000 g/mol.
 22. The process according to claim 19,characterized that the (meth) acrylic polymer (P1) has a mass averagemolecular weight Mw between 6 000 g/mol and 50 000 g/mol.
 23. Animpregnation process for impregnating a fibrous substrate, wherein saidfibrous substrate comprises long fibres and said process comprises astep of impregnating said fibrous substrate with a liquid compositioncomprising: a) a (meth)acrylic polymer (P1), b) a multistage polymer andc) a (meth)acrylic monomer (M1) wherein the multistage polymer tomonomer ratio by weight in the liquid composition is between 1/99 and25/75.
 24. The impregnation process according to claim 23, characterizedthat the (meth)acrylic polymer (P1) has a mass average molecular weightMw of less than 100 000 g/mol.
 25. The impregnation process according toclaim 23, characterized that the (meth)acrylic polymer (P1) has a massaverage molecular weight Mw between 5 000 g/mol and 70 000 g/mol. 26.The impregnation process according to claim 23, characterized that the(meth)acrylic polymer (P1) has a mass average molecular weight Mwbetween 6 000 g/mol and 50 000 g/mol.
 27. (canceled)
 28. (canceled) 29.(canceled)
 30. (canceled)
 31. The composition according to claim 18wherein the polyethylene glycol group of the polyethylene glycol (meth)acrylates has a molecular weight ranging from 400 g/mol to 10 000 g/mol.